Morero oa ho lemoha | Lenane la tshebetso | Boleng bo lekantsoeng | |
Karolelano ea ho fokotsa metsi % | ≥14 | ≥20 | |
Sekhahla sa ho tsoa mali % | ≤90 | ≤80 | |
Litaba tsa khase % | ≤3.0 | ≤2.0 | |
Lekhalo la nako ea condense (min) | Konyana ea pele | -90 ~ 120 | -90 ~ 120 |
Qetello ea ho qetela | |||
Karolelano ea matla a hatellang% | 1d | ≥140 | ≥160 |
3d | ≥130 | ≥150 | |
7d | ≥125 | ≥140 | |
28d | ≥120 | ≥130 | |
Karolelano ea sekhahla sa ho fokotseha % | ≤135 | ≤135 | |
Corrosion effect bakeng sa tšepe | Ha ho letho | Ha ho letho | |
Uniformity index | Morero oa ho lemoha | snf Powder Index | |
Litaba tse tiileng (%) | ≥92 | ||
Boikoetliso (%) | 0.315mm (masala)<10 | ||
PH boleng(10g/L) | 7--9 | ||
Likahare tsa chlorine ion(%) | ≤0.5 | ||
Sodium sulfate (%) | ≤5 | ||
Kakaretso ea litaba tsa alkali(%) | ≤20 | ||
Insoluble matter(%) | ≤0.5 | ||
Mokelikeli oa samente (mm) | ≥220 | ||
Ponahalo | Phofo e mosehla-sootho |
E sebelisoa haholo boenjiniere ba konkreite, prefabricated, sleeper, marokho, lithanele, tšireletso ea naha, boenjiniere ba sesole, paballo ea metsi, boenjiniere ba matla, liteishene tsa boema-kepe, tsela ea lifofane, boenjiniere ba meaho e phahameng.
Tekanyetso:0.5% -0.8%, mosebelisi o lokela ho latela tlhoko ea ho etsa liteko ho fumana tekanyo e nepahetseng.
Plasticity e Hlollang: Ho latela lipalo-palo, matla a khatello ka letsatsi la 1, letsatsi la 3 le la 28 kamora ts'ebeliso e le 'ngoe a eketsoa ka 60% -90% le 25% -60% ka ho latellana ha e eketsoa ka litekanyetso tse tloaelehileng tsa motsoako.Ka lebaka leo, matla a khatello, matla a ho tsitsa, matla a buckling le modulus ea elasticity e tla ntlafatsoa ho isa bohōleng bo itseng.
Tlas'a boemo ba karo-karolelano ea metsi / samente, collapsibility e ka eketsoa ka makhetlo a 5-8 ha e eketsoa ka tekanyo ea 0.75% ea motsoako.
15-20% ea samente e ka bolokoa ha moemeli a kopantsoe ka tekanyo ea motsoako oa 0.75%, e behiloeng pele ke ho putlama le matla a tšoanang.